231e670e-360d-4f1e-9d62-7a1e35ac4b27 砖块，烧结砖 brick, sintered brick 烧结法，原材料破碎、混合-压制工艺-干燥工艺-烧结工艺 raw material crushing, mixing, pressing process, drying process, sintering process 生产混合，在工厂 production mix, at plant Manufacturing Manufacture of other non-metallic mineral products Manufacture of non-metallic mineral products n.e.c. Manufacture of refractory products 烧结砖的生产工艺流程分别为烧结法，原材料破碎、混合-压制工艺-干燥工艺-烧结工艺 The production process of sintered bricks are sintering method, raw material crushing, mixing - pressing process - drying process - sintering process ad8a7d26-873a-44b5-ac17-786e1fd1d241 1 2020 WDC（水基钻屑） 用于替代天然粘土制备烧结砖。通过压滤机预处理，WDC 的含水量可从 80% 降至 20%，从而满足对外交付的循环利用要求。WDC 中剩余的水可直接用于制砖（240 毫米 × 115 毫米 × 53 毫米），以减少水资源的消耗。整个生产过程包括原料制备、混合、压制、干燥和烧结（温度为 800-1000 ℃；时间为 1-4 h）。 WDC（water-based drilling cuttings） were used as a replacement for natural clay to prepare sintered bricks. The water content of the WDC can be reduced from 80% to 20% through press filter pretreatment, which can meet the requirements of external delivery for recycling. The remaining water in the WDC can be used directly to make bricks (240 mm × 115 mm × 53 mm) to reduce the consumption of water resources. The entire production process includes raw material preparation, mixing, pressing, drying and sintering (temperature of 800–1000 °C; time for 1-4 h) 0.19519812609798945 sintered bricks; sintering process; production mix, at plant 烧结砖; 烧结工艺; 生产混合，在工厂 1 sintered bricks; raw materials processing (crushing, mixing); production mix, at plant 烧结砖; 原材料加工（破碎、混合）; 生产混合，在工厂 sintered bricks; drying process; production mix, at plant 烧结砖; 干燥工艺; 生产混合，在工厂 sintered bricks; pressing process; production mix, at plant 烧结砖; 压制工艺; 生产混合，在工厂 Partly terminated system Attributional 所有主要原材料和基本能源都包括在内。原材料和能源流量非常小（小于 1%）的生产过程不包括在内。这些截止标准不适用于危险材料和物质。 All major raw materials and all the essential energy is included. The production processes for raw materials and energy flows with very small amounts (less than 1%) are not included. These cut-off criteria do not apply for hazardous materials and substances. Liu, W. et al. Comparative life cycle assessment of cement, sintered bricks and non-sintered bricks manufacturing using water-based drilling cuttings from shale gas production in the Sichuan Basin, China. J. Environ. Manage. 314, 115135 (2022). Liu, W. et al. Comparative life cycle assessment of cement, sintered bricks and non-sintered bricks manufacturing using water-based drilling cuttings from shale gas production in the Sichuan Basin, China. J. Environ. Manage. 314, 115135 (2022). The internal review was done by several iteration steps concerning raw data validation, raw data documentation, representativity, completeness and consistency of modelling with regard to ISO 14040 and 14044. 内部审查通过几个迭代步骤完成，涉及原始数据验证、原始数据记录、代表性、完整性、与 ISO 14040 和 14044 有关的建模的一致性。 wang xiangjin 王湘锦 Liu, W. et al. Comparative life cycle assessment of cement, sintered bricks and non-sintered bricks manufacturing using water-based drilling cuttings from shale gas production in the Sichuan Basin, China. J. Environ. Manage. 314, 115135 (2022). ILCD Data Network - Entry-level Fully compliant Fully compliant Fully compliant Fully compliant Fully compliant Fully compliant Tiangong LCA Data Working Group 天工LCA数据团队 用于计算烧结砖生产过程的相关环境影响 For calculating the environmental impacts associated with the production process of sintered bricks 2024-12-06T15:27:24+08:00 ILCD format wang xiangjin 王湘锦 01.01.000 https://lcdn.tiangong.earth/datasetdetail/model.xhtml?uuid=6e82a077-ce52-40d4-a12d-10999e3d35e0&version=01.01.000 Tiangong LCA Data Working Group 天工LCA数据团队 No Free of charge for all users and uses